Development of mix design method based on statistical analysis of different factors for geopolymer concrete

The present study proposes the mix design method of Fly Ash (FA) based geopolymer concrete using Response Surface Methodology (RSM). In this method, different factors, including binder content, alkali/binder ratio, NS/NH ratio (sodium silicate/sodium hydroxide), NH molarity, and water/solids ratio were considered for the mix design of geopolymer concrete. The 2D contour plots were used to setup the mix design method to achieve the target compressive strength. The proposed mix design method of geopolymer concrete is divided into three categories based on curing regime, specifically one ambient curing (25 °C) and two heat curing (60 and 90 °C). The proposed mix design method of geopolymer concrete was validated through experimentation of M30, M50, and M70 concrete mixes at all curing regimes. The observed experimental compressive strength results validate the mix design method by more than 90% of their target strength. Furthermore, the current study concluded that the required compressive strength can be achieved by varying any factor in the mix design. In addition, the factor analysis revealed that the NS/NH ratio significantly affects the compressive strength of geopolymer concrete.     

C105管桩混凝土设计参数取值的探讨

通过试验得出了C105混凝土100 mm×100 mm×100 mm立方体非标准试件抗压强度换算系数以及C105混凝土的标准方差和强度变异系数。采用理论计算,得到了棱柱体抗压强度与立方体抗压强度的比值α_c1,并与试验实测平均值进行了比较,验证了理论计算方法的可行性。此外,通过对比分析,探讨了直接外延法和引用公式法两种C105混凝土设计参数计算方法的正确性,研究结果可为C105管桩混凝土的设计和应用提供参考。     

浅谈箱梁模板混凝土浇筑防漏装置施工

传统的箱梁模板混凝土浇筑施工工艺中,由于模板为刚性,加工基座也为刚性,因此不可避免的存在缝隙而导致漏浆,形成梁体的麻面、竖横等,影响梁体美观甚至梁的强度。通过对箱梁模板预制浇筑工艺的探索和研究,最终根据其施工特点研制出了箱梁模板混凝土浇筑防漏装置,极大程度的减少了漏浆现象的发生,同时该装置也有着结构简洁,取材方便,利于推广的优点。     

C50混凝土推定抗压强度的概率统计分析

在对广州某施工现场进行混凝土回弹试验的基础上,采用χ2检验法对现场采集到的混凝土抗压强度选取正态分布进行检验,本文分析C50混凝土推定抗压强度的概率统计规律,计算结果表明,施工现场的C50混凝土推定抗压强度的概率分布服从正态分布,与规范中C50混凝土抗压强度的均值,变异系数相比,该C50混凝土抗压强度的离散型较小。     

填充系数对橡胶连续塑炼机塑炼效果的影响

以新型连续塑炼机为实验平台,天然橡胶为生胶原料,考察了填充系数对天然橡胶连续塑炼效果的影响。结果表明,在塑炼段、销钉段和挤出段3段机筒和机头冷却水温度依次为40,50,60,70℃,转子转速为30 r/min,填充系数为60%的工艺条件下,连续塑炼机具有最好的塑炼效果,天然橡胶门尼黏度的下降幅度最大,塑炼胶更加均匀。     

玄武岩短纤维增强硅橡胶复合材料的制备及性能

采用玄武岩短纤维(BF)增强硅橡胶,制备了BF/硅橡胶复合材料,考察了硅烷偶联剂的种类、BF用量以及硫化条件对复合材料力学性能的影响,并用扫描电子显微镜观察了复合材料的微观形貌。结果表明,用KH 550对BF进行表面处理,所得复合材料的力学性能优于以Si 69处理的材料;当BF用量为20份时,BF/硅橡胶复合材料的力学性能最好;制备复合材料的最佳硫化条件为10 MPa×175℃×25 min;用KH 550处理BF,BF与硅橡胶的相容性比用Si 69处理的好。     

不同硫化体系天然橡胶硫化胶的机械力-化学再生及性能

研究了普通硫黄硫化体系(CV)、半有效硫化体系(SEV)和有效硫化体系(EV)硫化天然橡胶(NR)的机械力-化学再生,采用化学探针试剂法分析了3种硫化体系NR硫化胶及其再生硫化胶的交联键类型及其分布,考察了再生胶的硫化特性、力学性能、动态力学性能,并用傅里叶变换红外光谱对其结构进行了分析。结果表明,EV硫化体系NR的硫化时间最短,CV硫化体系最长。CV硫化体系硫化胶的多硫键含量最高,EV硫化体系单硫键含量最高,SEV硫化体系介于两者之间;在NR进行机械力-化学再生过程中,交联键的破坏以键能较低的多硫键为主。CV硫化体系NR再生硫化胶的再生效果好,力学性能佳,储能模量低,损耗因子高。     

充油溶聚丁苯橡胶2564 A的微观结构与性能

研究了溶聚丁苯橡胶(SSBR,牌号为2564 A)的微观结构与性能,并与牌号为5025-2的SSBR及乳聚丁苯橡胶(ESBR,牌号为1712)进行了对比。结果表明,与ESBR 1712相比,SSBR 2564 A生胶的数均分子量和重均分子量大,分子量分布窄,乙烯基和顺式结构含量高、反式结构含量低,混炼胶的硫化速率慢,硫化胶的物理机械性能略差,耐老化性能、压缩生热性能及炭黑分散性优;与SSBR 5025-2相比,SSBR 2564 A生胶的数均分子量、重均分子量及分子量分布相当,乙烯基含量高,顺式结构含量略高,反式结构含量低,混炼胶的结合胶含量高,交联密度相当,硫化速率略快,硫化胶的物理机械性能相当,耐老化性能优,压缩生热性能及炭黑分散性相当。     

增容高抗冲聚苯乙烯/高乙烯基聚丁二烯橡胶热塑性硫化胶的Mullins效应及其可逆性

采用动态硫化法制备了苯乙烯-丁二烯-苯乙烯嵌段共聚物(SBS)增容高抗冲聚苯乙烯(HIPS)/高乙烯基聚丁二烯橡胶(HVPBR)热塑性硫化胶(TPV),考察了SBS用量对TPV物理机械性能的影响,表征了TPV的微观形貌,并研究了TPV的Mullins效应及其可逆性。结果表明,SBS可显著改善HIPS/HVPBR体系的相容性,其用量为12份时,TPV的物理机械性能较好;SBS增容TPV的断面平整、结构致密,界面相互作用明显增强;SBS增容TPV在循环单轴拉伸过程中出现明显的Mullins效应,提高应变速率时,TPV的最大应力和内耗呈增大趋势,瞬时残余形变则减小;当拉伸比相同时,TPV经第1次拉伸热处理后,第2次单轴拉伸中TPV的最大应力和内耗均增大,瞬时残余形变则减小。     

乙烯-乙酸乙烯酯共聚物/氢化丁腈橡胶共混物的相态结构和低温性能研究

采用熔融共混法制备乙烯-乙酸乙烯酯共聚物(EVM)/氢化丁腈橡胶(HNBR)共混物,研究其硫化特性、相态结构、动态力学性能、物理性能和低温拉伸性能。结果表明:当EVM/HNBR共混比为70/30时,EVM形成连续相,HNBR形成分散相;随着HNBR用量的增大,HNBR相态由分散相向连续相转变。HNBR的加入可以提高EVM的耐低温性能,当EVM/HNBR共混比为30/70时,共混物-40℃下的低温拉断伸长率可达300%左右。差示扫描量热分析表明,随着HNBR用量的增大,共混物玻璃化温度降低。